Absorption and diffusion of carbon into solid ferrous alloys by heating, to a temperature usually above AC3, in contact with a suitable carbonaceous material. A form of case hardening that produces a carbon gradient extending inward from the surface, enabling the surface layer to be hardened either by quenching directly from the carburizing temperature or by cooling to room temperature, then reaustenitizing and quenching.
Have a Question or Need a Quote?
Pinson Valley Heat Treating Co. has been servicing the fabricating, machining, forging, and casting industries as well as other similar customers around the southeast since 1970. The employees at PVHT are dedicated to Quality Work, Quick Service, at a Fair Price. If you have a question or have something we can be of service, please give us a call Monday thru Friday 7:30 am-4:00 pm